Did 5.25" floppies undergo a change in magnetic coating?
3.5" floppy disks, in the transition from 720K to 1.44M, changed the actual coating to a different compound that was magnetically 'stiffer'. This was necessary to support the higher density, but meant the old disks could not support the new high-density format even if used in a new drive. A more subtle and much nastier problem: if you formatted a new disk in an old drive, everything would seem fine, but the information would not have been recorded strongly enough, and might fade over the next few days.
5.25" floppies made several format transitions that together accomplished an order of magnitude capacity increase until the final 1.2M format. Did any of these transitions involve a similar change in the actual coating? Or did the disks themselves stay interchangeable apart from issues of hard versus soft sectors?
history hardware floppy-disk
asked 6 hours ago
rwallacerwallace
9,375446137
add a comment |
3.5" floppy disks, in the transition from 720K to 1.44M, changed the actual coating to a different compound that was magnetically 'stiffer'. This was necessary to support the higher density, but meant the old disks could not support the new high-density format even if used in a new drive. A more subtle and much nastier problem: if you formatted a new disk in an old drive, everything would seem fine, but the information would not have been recorded strongly enough, and might fade over the next few days.
5.25" floppies made several format transitions that together accomplished an order of magnitude capacity increase until the final 1.2M format. Did any of these transitions involve a similar change in the actual coating? Or did the disks themselves stay interchangeable apart from issues of hard versus soft sectors?
history hardware floppy-disk
asked 6 hours ago
rwallacerwallace
9,375446137
add a comment |
3.5" floppy disks, in the transition from 720K to 1.44M, changed the actual coating to a different compound that was magnetically 'stiffer'. This was necessary to support the higher density, but meant the old disks could not support the new high-density format even if used in a new drive. A more subtle and much nastier problem: if you formatted a new disk in an old drive, everything would seem fine, but the information would not have been recorded strongly enough, and might fade over the next few days.
5.25" floppies made several format transitions that together accomplished an order of magnitude capacity increase until the final 1.2M format. Did any of these transitions involve a similar change in the actual coating? Or did the disks themselves stay interchangeable apart from issues of hard versus soft sectors?
history hardware floppy-disk
asked 6 hours ago
rwallacerwallace
9,375446137
3.5" floppy disks, in the transition from 720K to 1.44M, changed the actual coating to a different compound that was magnetically 'stiffer'. This was necessary to support the higher density, but meant the old disks could not support the new high-density format even if used in a new drive. A more subtle and much nastier problem: if you formatted a new disk in an old drive, everything would seem fine, but the information would not have been recorded strongly enough, and might fade over the next few days.
5.25" floppies made several format transitions that together accomplished an order of magnitude capacity increase until the final 1.2M format. Did any of these transitions involve a similar change in the actual coating? Or did the disks themselves stay interchangeable apart from issues of hard versus soft sectors?
history hardware floppy-disk
history hardware floppy-disk
asked 6 hours ago
rwallacerwallace
9,375446137
asked 6 hours ago
rwallacerwallace
9,375446137
asked 6 hours ago
rwallacerwallace
9,375446137
asked 6 hours ago
rwallacerwallace
9,375446137
asked 6 hours ago
rwallacerwallace
9,375446137
9,375446137
add a comment |
add a comment |
1 Answer
1
active
oldest
votes
The main technical parameter for a floppy disk's coating is its coercitiviy, i.e. the resistance of ferromagnetic matter to withstand demagnetization. Coercitivity is measured in Oersted, after Hans Christian Ørsted, a Danish physicist who discovered the magnetic impact of electrical current.
- 5 1/4" disks storing 360K and 720K (SD and DD) used a coating with a coercitivity of 300 Oersted.
- 5 1/4 disks storing 1.2M used a coating with a coercitivity of 600 Oersted.
So yes, the coating was changed to support the HD format.
The difference between 5 1/4" DD and HD coating is much larger than the same difference between 3 1/2" DD and HD media - which is 660 Oe an 720 Oe, respectively.
answered 4 hours ago
tofrotofro
15.7k33190
add a comment |
Your Answer
StackExchange.ready(function() {
var channelOptions = {
tags: "".split(" "),
id: "648"
};
initTagRenderer("".split(" "), "".split(" "), channelOptions);
StackExchange.using("externalEditor", function() {
// Have to fire editor after snippets, if snippets enabled
if (StackExchange.settings.snippets.snippetsEnabled) {
StackExchange.using("snippets", function() {
createEditor();
});
}
else {
createEditor();
}
});
function createEditor() {
StackExchange.prepareEditor({
heartbeatType: 'answer',
autoActivateHeartbeat: false,
convertImagesToLinks: false,
noModals: true,
showLowRepImageUploadWarning: true,
reputationToPostImages: null,
bindNavPrevention: true,
postfix: "",
imageUploader: {
brandingHtml: "Powered by u003ca class="icon-imgur-white" href="https://imgur.com/"u003eu003c/au003e",
contentPolicyHtml: "User contributions licensed under u003ca href="https://creativecommons.org/licenses/by-sa/3.0/"u003ecc by-sa 3.0 with attribution requiredu003c/au003e u003ca href="https://stackoverflow.com/legal/content-policy"u003e(content policy)u003c/au003e",
allowUrls: true
},
noCode: true, onDemand: true,
discardSelector: ".discard-answer"
,immediatelyShowMarkdownHelp:true
});
}
});
Sign up or log in
StackExchange.ready(function () {
StackExchange.helpers.onClickDraftSave('#login-link');
});
Sign up using Google
Sign up using Facebook
Sign up using Email and Password
Post as a guest
Required, but never shown
StackExchange.ready(
function () {
StackExchange.openid.initPostLogin('.new-post-login', 'https%3a%2f%2fretrocomputing.stackexchange.com%2fquestions%2f9300%2fdid-5-25-floppies-undergo-a-change-in-magnetic-coating%23new-answer', 'question_page');
}
);
Post as a guest
Required, but never shown
1 Answer
1
active
oldest
votes
1 Answer
1
active
oldest
votes
active
oldest
votes
active
oldest
votes
The main technical parameter for a floppy disk's coating is its coercitiviy, i.e. the resistance of ferromagnetic matter to withstand demagnetization. Coercitivity is measured in Oersted, after Hans Christian Ørsted, a Danish physicist who discovered the magnetic impact of electrical current.
- 5 1/4" disks storing 360K and 720K (SD and DD) used a coating with a coercitivity of 300 Oersted.
- 5 1/4 disks storing 1.2M used a coating with a coercitivity of 600 Oersted.
So yes, the coating was changed to support the HD format.
The difference between 5 1/4" DD and HD coating is much larger than the same difference between 3 1/2" DD and HD media - which is 660 Oe an 720 Oe, respectively.
answered 4 hours ago
tofrotofro
15.7k33190
add a comment |
The main technical parameter for a floppy disk's coating is its coercitiviy, i.e. the resistance of ferromagnetic matter to withstand demagnetization. Coercitivity is measured in Oersted, after Hans Christian Ørsted, a Danish physicist who discovered the magnetic impact of electrical current.
- 5 1/4" disks storing 360K and 720K (SD and DD) used a coating with a coercitivity of 300 Oersted.
- 5 1/4 disks storing 1.2M used a coating with a coercitivity of 600 Oersted.
So yes, the coating was changed to support the HD format.
The difference between 5 1/4" DD and HD coating is much larger than the same difference between 3 1/2" DD and HD media - which is 660 Oe an 720 Oe, respectively.
answered 4 hours ago
tofrotofro
15.7k33190
add a comment |
The main technical parameter for a floppy disk's coating is its coercitiviy, i.e. the resistance of ferromagnetic matter to withstand demagnetization. Coercitivity is measured in Oersted, after Hans Christian Ørsted, a Danish physicist who discovered the magnetic impact of electrical current.
- 5 1/4" disks storing 360K and 720K (SD and DD) used a coating with a coercitivity of 300 Oersted.
- 5 1/4 disks storing 1.2M used a coating with a coercitivity of 600 Oersted.
So yes, the coating was changed to support the HD format.
The difference between 5 1/4" DD and HD coating is much larger than the same difference between 3 1/2" DD and HD media - which is 660 Oe an 720 Oe, respectively.
answered 4 hours ago
tofrotofro
15.7k33190
The main technical parameter for a floppy disk's coating is its coercitiviy, i.e. the resistance of ferromagnetic matter to withstand demagnetization. Coercitivity is measured in Oersted, after Hans Christian Ørsted, a Danish physicist who discovered the magnetic impact of electrical current.
- 5 1/4" disks storing 360K and 720K (SD and DD) used a coating with a coercitivity of 300 Oersted.
- 5 1/4 disks storing 1.2M used a coating with a coercitivity of 600 Oersted.
So yes, the coating was changed to support the HD format.
The difference between 5 1/4" DD and HD coating is much larger than the same difference between 3 1/2" DD and HD media - which is 660 Oe an 720 Oe, respectively.
answered 4 hours ago
tofrotofro
15.7k33190
edited 3 hours ago
answered 4 hours ago
tofrotofro
15.7k33190
answered 4 hours ago
tofrotofro
15.7k33190
answered 4 hours ago
tofrotofro
15.7k33190
15.7k33190
add a comment |
add a comment |
Thanks for contributing an answer to Retrocomputing Stack Exchange!
- Please be sure to answer the question. Provide details and share your research!
But avoid …
- Asking for help, clarification, or responding to other answers.
- Making statements based on opinion; back them up with references or personal experience.
To learn more, see our tips on writing great answers.
Sign up or log in
StackExchange.ready(function () {
StackExchange.helpers.onClickDraftSave('#login-link');
});
Sign up using Google
Sign up using Facebook
Sign up using Email and Password
Post as a guest
Required, but never shown
StackExchange.ready(
function () {
StackExchange.openid.initPostLogin('.new-post-login', 'https%3a%2f%2fretrocomputing.stackexchange.com%2fquestions%2f9300%2fdid-5-25-floppies-undergo-a-change-in-magnetic-coating%23new-answer', 'question_page');
}
);
Post as a guest
Required, but never shown
Sign up or log in
StackExchange.ready(function () {
StackExchange.helpers.onClickDraftSave('#login-link');
});
Sign up using Google
Sign up using Facebook
Sign up using Email and Password
Post as a guest
Required, but never shown
Sign up or log in
StackExchange.ready(function () {
StackExchange.helpers.onClickDraftSave('#login-link');
});
Sign up using Google
Sign up using Facebook
Sign up using Email and Password
Post as a guest
Required, but never shown
Sign up or log in
StackExchange.ready(function () {
StackExchange.helpers.onClickDraftSave('#login-link');
});
Sign up using Google
Sign up using Facebook
Sign up using Email and Password
Sign up using Google
Sign up using Facebook
Sign up using Email and Password
Post as a guest
Required, but never shown
Required, but never shown
Required, but never shown
Required, but never shown
Required, but never shown
Required, but never shown
Required, but never shown
Required, but never shown
Required, but never shown